The application of self-compacting concrete in massive structures is still low due to the perceived high cracking tendency associated with high shrinkage and heat of cement hydration. This conclusion is from short-term research work of up to 3 months after casting. The …
jp, Kenya
(code pays fourni par la source)
Accès ouvert
2023
article
OpenAlex
Aghiad Alhafez, S. Miyazawa, Nobukazu NITO, Ryuichiroh Kuga et autres
Cement with fly ash has rarely been used in Japan, mainly because its strength development is slower than ordinary Portland cement. In this research, the effect of the new type of fly ash (which was modified by the electrostatic belt separation method) …
jp
(code pays fourni par la source)
Accès ouvert
2023
preprint
OpenAlex
Aghiad Alhafez, S. Miyazawa, Nobukazu NITO, Ryuichiroh Kuga et autres
Fly ash cement has rarely been used in Japan, mainly because its strength development is slower than ordinary Portland cement. In this research, the effect of the new fly ash cement with both high alite (C3S) cement and fly ash modified by …
jp
(code pays fourni par la source)
Accès ouvert
2023
article
OpenAlex
Minoru Hata, Makoto Sato, S. Miyazawa
本研究は，フライアッシュ，高炉スラグ微粉末及びアルカリ刺激剤として水酸化カルシウム等を使用した結合材（IBPM）を，蒸気養生により製造される様々なプレキャストコンクリート（PCa）製品に適用することを目的としたものである．IBPMコンクリートの圧縮強度に及ぼすフライアッシュの品質変動の影響，水結合材比と圧縮強度の関係について明らかにするとともに，収縮特性，塩化物イオン拡散係数，硫酸抵抗性，耐摩耗性，凍結融解抵抗性について実験により検討した．さらに，ボックスカルバート，セグメント，ヒューム管，マンホールの実物大供試体の製造において，通常の振動締固め及び遠心力締固めによる締固めが可能であること，これらのPCa製品が十分な耐荷力を有していることを示した．
Accès ouvert
2022
article
OpenAlex
Minoru Hata, Makoto Sato, S. Miyazawa
The purpose of this study was to apply a cementless binder using industrial by-products (fly ash, ground-granulated blast furnace slag, and silica fume) to precast concrete products. In this binder, calcium hydroxide was included as an alkali stimulant but Portland cement was …
jp
(code pays fourni par la source)
Accès ouvert
2022
article
OpenAlex
Gerald Gyabaah, S. Miyazawa, Nobukazu NITO
Usage of industrial by-products such as ground granulated blast furnace slag (GGBFS), gypsum, and limestone powder have gained prominence in concrete production. It is, therefore, very important to conduct research into the various materials and their attendant influence on properties of concrete …
jp
(code pays fourni par la source)
2021
book-chapter
OpenAlex
Hideki Igawa, Minoru Hata, Katsumi Sugimoto, Etsuro Hayashi et autres
Accès ouvert
2021
article
OpenAlex
Minoru Hata, Katsumi Sugimoto, Etsuro HAYASHI, S. Miyazawa
循環型社会や低炭素社会の構築が叫ばれる中、産業副産物の有効活用とCO2排出量の抑制が可能で、100年相当の高耐久性を有するプレキャスト製品の創出を目指して本研究に着手した。その結果、フライアッシュと高炉スラグ微粉末を中心に、下水汚泥焼却灰の粒度調整灰とシリカフュームを加えた計4種類の産業副産物に水酸化カルシウム（消石灰）と膨張材を添加した結合材を考案した。この結合材をセメント代替として用いた硬化体を下水道管に適用することを目的とし、耐硫酸性や耐塩害性などについて検討した。その結果、セメントコンクリートよりも耐硫酸性が優れることを確認し、耐塩害性も有するものと推察した。
jp
(code pays fourni par la source)
Accès ouvert
2021
article
OpenAlex
Minoru Hata, Katsumi Sugimoto, Etsuro HAYASHI, Yukitoshi IWASA et autres
本研究は，セメントを使わない硬化体（IBPM）を用いた下水道管の実用化を図ると共に，様々なプレキャストコンクリート製品へのIBPMの適用も視野に入れた検討を行うことを目的としている．IBPMにはフライアッシュと高炉スラグ微粉末を中心に，下水汚泥焼却灰の粒度調整灰とシリカフュームを加えた4種類の産業副産物を用い，アルカリ刺激剤として水酸化カルシウム，収縮低減用に膨張材を添加している．本研究では，蒸気養生を行ったIBPMモルタルの強度発現性に及ぼす構成材料と混合比率の影響を評価した．また，IBPM製ヒューム管の実物大供試体による水理実験を実施した結果，塩化ビニール管と同等の粗度係数が得られた．また，IBPM製RC梁の曲げ載荷実験により，セメントを用いた場合と同等の曲げ性状を有することが明らかとなった．
Accès ouvert
2020
article
OpenAlex
Bernard A. Zulu, S. Miyazawa, Nobukazu NITO
Thermal stresses are generated in concrete during the accelerated curing process in precast concrete. These stresses may cause concrete to crack, which would have a negative effect on the general concrete performance. This paper provides the results of the thermal stress analysis …
jp
(code pays fourni par la source)
2020
book-chapter
OpenAlex
Minoru Hata, Katsumi Sugimoto, Etsuro Hayashi, S. Miyazawa et autres
2020
book-chapter
OpenAlex
Minoru Hata, Katsumi Sugimoto, Etsurou Hayashi, S. Miyazawa