Thermal Processing Limits in Oxide-Channel Ferroelectric Field Effect Transistors

Le résumé fourni par la source

In this work, we report a systematic study of the impact of high-temperature post-capping thermal annealing on the memory characteristics of Oxide-semiconductor channel ferroelectric field-effect transistors (OS-FeFETs). Using an identical engineered ferroelectric gate stack 8nm Hf0.5Zr0.5O2 (HZO) / 3 nm Al2O3 / 8 nm HZO (8/3/8) and a hybrid capping layer (3 nm HfO2 + 3 nm Al2O3), 10 percent Ga doped InO (IGO) channel and 4 percent W doped InO (IWO) channel FeFETs remain functional after annealing at temperatures up to 650 C for durations of up to 30 min and 10 min, respectively; further annealing results in irreversible loss of conduction and device failure. Detailed electrical analysis reveals that the MW enhancement originates from a preferential positive shift in the erased-state threshold voltage, while the programmed-state threshold voltage remains comparatively stable. Grazing-incidence X-ray diffraction measurements further indicate structural evolution in the IWO and IGO oxide channels with increasing annealing temperature, supporting the observed electrical trends.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.