Shear bond strength of flowable composite posts on 0.019" x 0.025" stainless steel wires
Résumé fourni par la source
Excessive force during crimping can cause gabling of the wire. 30 samples each with 0.019'' x 0.025'' stainless steel wire were surface treated: sandblasted only; metal primed only; and both sandblasted and metal primed. Flowable composite posts were prepared on it. A universal mechanical testing machine was used to measure debond force. The mean shear bond strength for flowable composite posts on 0.019″ x 0.025″ stainless steel wires in this study was 16.29 MPa. It was 11.33 MPa with sandblasted wires and 8.51 MPa with metal primed wires. Sandblasting or metal priming increases the bond strength of flowable composites to stainless steel wires.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé ; titre concordant.
- Titre Crossref
- Shear bond strength of flowable composite posts on 0.019" x 0.025" stainless steel wires
- Date Crossref
- 31/08/2026
- Éditeur
- Biomedical Informatics
- Type
- journal-article
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude et ne compte pas comme une seconde source scientifique indépendante.
Institutions déclarées
Une affiliation ne permet pas de déduire la nationalité d’un auteur.