Nano- and Microplastic Release from Indoor Drinking Water Pipes: characteristics of different Pipe Materials

Le résumé fourni par la source

The current study comparatively evaluated the release characteristics of nano/microplastics and organic matter from non-metallic drinking water pipes. Accelerated aging experiments were conducted on polybutylene(PB) and impact-modified polyvinyl chloride(iPVC) to verify the effects of long-term operations on the pipe material. FT-IR spectra of particles detected after the aging conditions matched those of the original pipe materials, confirming the presence of pipe-derived particles. Subsequently, a continuous-flow system simulating drinking water distribution conditions was established, and a pipe circulation experiment was conducted for approximately 45 days under a residual chlorine concentration of about 4.3mg/L and a temperature of 40°C. The results showed that PB exhibited a higher cumulative release of nanoparticles and a greater number of microplastic particles than iPVC. Results also showed that the total organic carbon(TOC) release from was also higher in PB. In contrast, iPVC and stainless steel(STS) showed no substantial differences in TOC concentration or cumulative nanoparticle release. These findings demonstrate that the release characteristics of nano/microplastics and organic matter vary depending on pipe material under drinking water distribution conditions and suggest that the potential release of nano/microplastics should be considered when selecting materials for drinking water pipes.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.