Environmental Aging Mechanisms and Their Impact on the Mechanical Performance of Fiber-Reinforced Polymer Composites: A Comprehensive Review

Le résumé fourni par la source

Fiber-reinforced polymer (FRP) composites are extensively used in aerospace, civil engineering, and defense applications because of their low density, high specific strength, corrosion resistance, and structural design flexibility. However, prolonged exposure to hygrothermal conditions, ultraviolet (UV) radiation, and thermo-oxidative environments can progressively damage these materials, leading to mechanical degradation and shortened service life. This review examines environmental aging in FRP composites at the levels of the polymer matrix, fiber/matrix interface, and reinforcing fibers. Representative predictive models, finite element methods, and experimental characterization techniques are summarized, together with the evolution of mechanical properties under different aging conditions. Hygrothermal degradation is mainly associated with moisture diffusion, matrix swelling, and interfacial debonding, whereas UV and thermo-oxidative aging are largely governed by photo-oxidation and thermally activated free-radical reactions. These processes may induce chain scission, crosslinking, matrix embrittlement, and interface damage. Under coupled environmental exposure, degradation is not simply additive because moisture transport, oxidation kinetics, and failure pathways may interact. Future research should emphasize multiscale characterization, anti-aging modification, interface engineering, protective coatings, and reliability-oriented lifetime prediction.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.