Optimization of Heat Treatment Parameters in CA-50 Steel Rebars: Impact on Microstructure and Corrosion Resistance

Résumé fourni par la source

This study evaluates the influence of heat treatment parameters on the microstructure and corrosion resistance of CA-50 low-carbon steel rebars (0.20–0.25 wt.% C) processed by the Thermex route. A full 23 factorial design combined with response surface methodology was employed to investigate the effects of residence time (15–35 min), heating rate (5–15 °C/min), and soaking temperature (730–850 °C). Corrosion behavior was assessed by linear potentiodynamic polarization and electrochemical impedance spectroscopy in 3.5 wt.% NaCl solution. The corrosion potential (Ecorr) varied between −520.6 and −618.1 mV, with optimal values close to −535 mV obtained at low heating rates and short residence times. Polarization resistance (Rp) ranged from 70.4 kΩ to 166.6 MΩ, with the highest value observed for treatment at 790 °C, 10 °C/min, and 25 min, representing an increase of more than fivefold compared to the reference condition. Statistical analysis revealed that residence time and heating rate significantly affect Ecorr (R2 = 96.8%), while Rp is governed exclusively by residence time (p = 0.004). Microstructural analysis correlated refined and homogeneous ferritic–pearlitic structures with improved corrosion resistance, whereas grain coarsening led to severe electrochemical degradation.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.