Coupled Effect of Interfacial Grit Particles and TGO Amplitude on Bond-Coat Crack Propagation in Thermal Barrier Coatings

Résumé fourni par la source

Residual grit particles introduced during grit blasting are important process-induced defects that can significantly affect the interfacial damage evolution of thermal barrier coatings (TBCs) under thermal cycling; however, the coupled effects of thermally grown oxide (TGO) amplitude, grit size, and grit position on crack propagation in the bond coat (BC) remain insufficiently understood. In this work, a two-dimensional finite element model containing residual alumina grit particles was established to investigate the influence of these three factors on the radial stress distribution and crack growth behavior in the BC, and their individual contributions and interaction effects were further quantified using response surface methodology. The results showed that TGO morphology and interfacial grit defects jointly controlled the stress concentration and crack propagation behavior in the BC. Increasing the TGO amplitude intensified the radial tensile stress concentration in the BC and gradually shifted the critical stress region during thermal cycling. Larger grit particles further aggravated the local stress concentration near the grit tips, while the movement of grit particles toward the TGO peak led to a more pronounced increase in stress concentration and crack propagation tendency. The crack growth behavior was found to be consistent with the corresponding stress evolution characteristics. Response surface analysis further revealed that grit size and grit position had much stronger effects on crack propagation than TGO amplitude, and their interaction was the most significant among all factor combinations. The minimum crack length in the BC layer was obtained at a TGO amplitude of 0.01 mm, a grit size of 20 μm, and a position parameter of 0.752, and the predicted value agreed well with the finite element result. This study provides a comparative basis for interfacial damage assessment and grit-blasting parameter optimization in TBCs containing residual grit defects.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.