Comparative impedance analysis of cold sintered and conventionally sintered ZnO-BaTiO 3 composite
Rattachement africain : pk, kr, gb. Niveau de preuve : code pays fourni par la source.
Le résumé fourni par la source
In the present work, focusing on ZnO-BaTiO 3 composite, we did a comparative study of cold sintered (400 MPa, 300 °C for 1 h dwell time) and conventionally sintered (1100 °C for 1 h dwell time) samples. Impedance analysis conducted across a temperature range of 25–250 °C and a frequency range of 100 Hz to 1 M Hz, revealed higher grain boundary resistance and space charge in cold sintered samples. Activation energy for alternating conduction mechanism for cold sintered samples (0.22 eV) was calculated to be comparable to that of conventionally sintered samples (0.18 eV). The distinct role of cold sintered samples was explained by the presence of possible charged defects at their grain boundaries.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Le contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé, mais le titre doit être comparé manuellement.
- Titre Crossref
- Comparative impedance analysis of cold sintered and conventionally sintered ZnO-BaTiO <sub>3</sub> composite
- Date Crossref
- 30/04/2026
- Éditeur
- SAGE Publications
- Type
- journal-article
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude, et il ne compte pas comme une seconde source scientifique indépendante.
Les institutions déclarées
Une affiliation ne permet pas de déduire la nationalité d’un auteur.