Influence of Acetic Acid on Hydrogen Sulfide Corrosion Mechanisms of Mild Steel
Rattachement africain : us. Niveau de preuve : code pays fourni par la source.
Le résumé fourni par la source
The influence of 1,000 ppmm of acetic acid on the corrosion mechanisms of mild steel with up to 10 mbar (10,000 ppmv) of H2S with and without CO2 at atmospheric pressure was investigated using electrochemical and surface analysis techniques. The results showed that anodic reaction retardation caused by acetic acid in CO2 corrosion at low temperatures was not observed when H2S was present in an H2S/CO2 environment. The potentiodynamic sweeps for H2S/CO2 corrosion showed a retardation of the corrosion rate, which is thought to be caused by a thin mackinawite layer that is known to form in these conditions.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Le contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé ; titre concordant.
- Titre Crossref
- Influence of Acetic Acid on Hydrogen Sulfide Corrosion Mechanisms of Mild Steel
- Date Crossref
- 14/04/2026
- Éditeur
- Association for Materials Protection and Performance (AMPP)
- Type
- journal-article
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude, et il ne compte pas comme une seconde source scientifique indépendante.
Les institutions déclarées
Une affiliation ne permet pas de déduire la nationalité d’un auteur.