Electrochemical and thermal control of continuous phase transitions in P2-NaxNi1/3Mn2/3O2

Le résumé fourni par la source

Sodium layered oxides often undergo phase transformations involving ordering or disordering of Na+ upon desodiation, i.e., when cycled as a battery electrode. Accurately characterizing these phases is crucial for understanding functional properties, such as chemical diffusivity. In this work, we reveal that Na+-vacancy (dis)ordering in a layered oxide is intrinsically coupled to symmetry-changing phase transformations of the host structure. We examine the low-symmetry orthorhombic unit cell of P2-NaxNi1/3Mn2/3O2 (NNM) using both neutron and X-ray diffraction. Specifically, special sodium stoichiometries (x = 2/3 and 1/2) exhibit concomitant Na+-vacancy ordering and an orthorhombic distortion from the parent hexagonal unit cell. We then demonstrate that electrochemical desodiation drives symmetry-changing transformations in NNM that are linked to Na+-vacancy (dis)ordering, with evidence of second-order behavior observed near x = 2/3. Variable-temperature synchrotron X-ray diffraction further clarifies the coupling between Na+-vacancy disordering and orthorhombic-to-hexagonal phase transitions in NNM. Surprisingly, the temperature-driven phase transitions at x = 2/3 and 1/2 differ in character, appearing second-order and first-order, respectively. Our analysis of the phase transitions in NNM has fundamental consequences for sodium chemical diffusivity in the vicinity of the ordered phases and leads to design principles for modifying phase transition behavior in the broader class of intercalation electrodes.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.