Irradiation Driven Restructuring of Nanocrystalline ThO 2 and Th 1– x U x O 2 Thin Films

Le résumé fourni par la source

Irradiation induced structural changes of actinide oxide materials is a key consideration in their development and use as nuclear fuels. This study reported on the synthesis of ThO 2 and Th 1– x U x O 2 ( x = 0.15, 0.50) thin films, fabricated using electrospray-assisted solution combustion synthesis, and their responses to ion irradiation. Krypton ion irradiations, up to a fluence of 1 × 10 16 ions/cm 2, were carried out to simulate radiation damage induced by fission products in a reactor environment. Structural and chemical changes induced by irradiation were analyzed using high-resolution scanning transmission electron microscopy (STEM), energy-dispersive X-ray spectroscopy (EDS), and electron energy-loss spectroscopy (EELS). It was determined that the extent and nature of irradiation-induced damage are strongly correlated with the uranium content. ThO 2 films were most susceptible to radiation-induced damage, with significant cavity formation and delamination from the substrate at high fluence. Of the compositions studied, Th 0.85 U 0.15 O 2 films showed the highest stability, characterized by moderate grain growth and the absence of voids or severe defect structures. In contrast, Th 0.5 U 0.5 O 2 films accumulated extensive damage, including the formation of a nanocrystalline central region. EELS analysis indicated that oxygen displacement is the primary driver of structural degradation in Th 0.5 U 0.5 O 2 films. α-particle spectroscopy confirmed minimal actinide loss across all compositions, underscoring the mechanical robustness of the films. These findings provide insight into the irradiation-induced damage mechanisms in ThO 2 and Th 1– x U x O 2 systems, supporting their development as potential materials for nuclear fuels and irradiation-tolerant thin film targets in nuclear physics measurements.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.