Making high-W-content Ta-W alloys ductile via minor alloying of Hf
Rattachement africain : cn. Niveau de preuve : code pays fourni par la source.
Le résumé fourni par la source
Ta-based refractory alloys offer excellent high-temperature strength, but high W content significantly reduces room-temperature tensile ductility. Here for Ta-14W alloy with fracture strain of ∼5%, we demonstrate that a minor Hf addition significantly improves its ductility to over 30%. Firstly, Hf induces an asymmetric core structure of screw dislocation and reduces generalized stacking fault energy (GSFE), thereby promoting dislocation mobility and dislocation multiplication during plastic deformation. Secondly, Hf can strengthen grain boundaries (GBs) by preferentially segregating near GBs. Thirdly, Hf binds with O atoms to form HfO2 particles at GBs, lowering the risk of oxygen embrittlement. All these mechanisms offer insightful guide for the development of advanced Ta-W-based refractory alloys.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Le contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé ; titre concordant.
- Titre Crossref
- Making high-W-content Ta-W alloys ductile via minor alloying of Hf
- Date Crossref
- 24/12/2025
- Éditeur
- Informa UK Limited
- Type
- journal-article
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude, et il ne compte pas comme une seconde source scientifique indépendante.
Où se fait cette recherche
-
Xi'an Jiaotong University pays non établi dans la noticeUniversité ou école supérieure
Xi'an Jiaotong University.
Une affiliation ne permet pas de déduire la nationalité d’un auteur.