Printability and rheological properties of 3D printing ultra-high ductility magnesium phosphate cement-based composites

Le résumé fourni par la source

With the aim to develop a 3D printing ultra-high ductility magnesium phosphate cement-based composites (3DP-UHDMC), the effects of thixotropic agent type and dosage, magnesium-phosphate ratio (M/P), water-solid ratio (W/SO), powder-binder ratio (P/B), borax-MgO ratio (BO/M) and PE fiber volume content on the printability and rheological properties were studied. Furthermore, a correlation between printability parameters (filament width, tan θ ) and rheological characteristics (yield stress, consistency coefficient) was established to predict printability under varying rheological behaviors. The optimal mixture proportion for 3DP-UHDMC was identified and a comparative analysis of the mechanical properties of cast and printed specimens was then completed. Experimental results indicated the optimum mixture proportion for 3DP-UHDMC as below: attapulgite content of 10%, M/P of 2.5, W/SO of 0.10, P/B of 0.35, BO/M of 0.3, and PE fiber volume content of 1.5%. The relationship between the filament width and the dynamic yield stress is a negative power function. The tan θ and static yield stress, as well as the spread diameter and dynamic yield stress, exhibit a negative exponential function relationship. Printability factors can be characterized by rheological parameters and optimal printability occurs within specific rheological parameters ranges: dynamic yield stress (284.87-541.09Pa), static yield stress (3379.78-4996.16Pa), and consistency coefficient (643.99-1016.41Pa·s n ). Compared with cast specimens, printed specimens exhibited reduced compressive strength and lower ultimate tensile stress, yet exhibited enhanced ultimate tensile strain.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.