Stable, Efficient Iron Electrodeposition via Anion-Directed Control of Fe(II) Coordination

Le résumé fourni par la source

Traditional steelmaking processes consume about 7% of the world’s energy supply, with reduction of iron oxides into iron via blast furnaces representing the most energy-demanding and capital-intensive step. To economize and modularize iron reduction processes, we aim to develop an electrodeposition technique to reduce aqueous iron ions to metallic iron. However, the hydrogen reduction reaction (HER) occurs at a more positive standard reduction potential than the iron reduction reaction. In addition, aqueous Fe(II) cations easily precipitate at mildly acidic conditions (pH ≥ 3), which limits the deposition efficiency and degrades deposit quality. To address these challenges, we first search for anions that have intermediate coordination strength with Fe(II) based on the hard-soft acid-base theory, trading a slightly more negative Fe(II) reduction potential for a considerably broader pH stability range. We select citrate with predicted intermediate coordination strength, in combination with more weakly coordinating anions (e.g., SO 4 2- , Cl - ) to control the coordination structure of Fe 2+ for improved electrolyte stability and electrodeposition behavior. We find that citrate coordination stabilizes Fe 2+ -based electrolytes at higher pH conditions (4.8–5.5), significantly extending their shelf life while also suppressing HER during Fe electrodeposition by orders of magnitude. To measure Faradaic efficiencies (FE), we developed a straightforward, titration-based methodology to quantify the amount of deposited iron regardless of the rate of concurrent HER. Although coordination between citrate and Fe 2+ decreases the reduction potential of Fe(II), high FE (≥98%) was achieved at 10 mA cm -2 . FE and achievable deposition rates are tunable by both concentration and the ratio of Fe 2+ to citrate. In all cases, Raman spectroscopy and X-ray diffraction (XRD) reveal that iron deposition in citrate-containing electrolytes suppresses iron oxide/hydroxide precipitation, in contrast to deposits generated in citrate-free electrolytes. Overall, this work demonstrates that citrate-mediated anion coordination enables high-purity iron electrodeposition with increased FE, high current density, and improved electrolyte stability. This multi-anion coordination strategy provides a versatile framework for designing stable electrolyte and efficient metal electrodeposition.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.