Effect of Laser Shock Peening on High-Cycle Fatigue Performance and Residual Stress in DH36 Welded Joints

Le résumé fourni par la source

DH36 high-strength steel is widely used in shipbuilding and other fields due to its excellent strength, low-temperature toughness, wear resistance, and corrosion resistance. However, the harsh deep-sea environment seriously reduces the service life of welds. In this study we subjected DH36 welded joints to laser shock peening at three different energy levels (5 J, 7 J, 9 J) to investigate its effects on microhardness, microstructure, high-cycle fatigue, and residual stress of the DH36 welded joints. Results indicate that LSP can significantly enhance the surface microhardness of welded joints. Notably, the 7 J energy treatment increased the weld zone microhardness from 195 HV0.2 to 231 HV0.2 (18.5% improvement) and the heat-affected zone microhardness from 194 HV0.2 to 234 HV0.2 (20.6% improvement). Residual tensile stress on the specimen surface was offset and replaced by residual compressive stress after LSP. Concurrently, the high-cycle fatigue limit of the specimens was significantly improved, with the most pronounced improvement observed in specimens subjected to 5 J energy—increasing from 258 MPa to 295 MPa, representing an increase of 14.34%.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.