Dynamic Ni–O Bonding Induced by Orbital Degeneracy Breaking for Efficient Li 2 CO 3 Decomposition

Le résumé fourni par la source

Abstract Lithium carbonate, the primary discharge product in Li–CO 2 batteries with high thermodynamic stability and a wide band gap, leads to significant electrochemical inertness, limiting efficiency and cycle life. The strongly delocalized p z orbital at a lower‐energy HOMO level in Li 2 CO 3 causes weak coupling with the O‐p z orbitals, increasing decomposition resistance owing to d‐orbital degeneracy in high‐local‐symmetry catalysts. This study introduces metastable tetragonal‐pyramidal nickel sulfide (tp‐NiS) with low‐symmetry NiS 5 coordination, breaking d‐orbital degeneracy and bringing d z 2 , d xz , and d yz orbitals closer to the Fermi level. Enhanced orbital overlap with Li 2 CO 3 O‐p z orbitals facilitates robust Ni–O bond formation. In situ spectroscopy confirms reversible Ni–O bond formation during cycling, ensuring electron transfer and complete Li 2 CO 3 decomposition. Conversely, weak interfacial interactions in octahedral NiS with highly symmetric local coordination only allow decomposition‐resistant Li 2 CO 3 and interface passivation. Consequently, tp‐NiS exhibits superior electrochemical performance, with the best reported reversibility and stability, a charge potential below 4.0 V, and 92.03% capacity retention after 1800 h. This metal redox‐driven mechanism establishes a reversible geometric conversion pathway, emphasizing the critical role of symmetry‐engineered Ni–O interactions in bifunctional catalysts.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.