Performance Enhancement in Carbon-Based All-Inorganic Perovskite Solar Cells via a Multifunctional Additive

Le résumé fourni par la source

Carbon-based, hole-transport-layer-free (HTL-free) all-inorganic perovskite solar cells (C-IPSCs) encounter several challenges, including poor crystallization quality, severe surface defects that trigger nonradiative recombination, and phase instability under ambient conditions. These issues limit their efficiency and long-term stability. In this study, we propose a one-step antisolvent method that incorporates guanabenz acetate salt (GBA) as a multifunctional additive to fabricate efficient CsPbI 1.8 Br 1.2 C-IPSCs. The C═O and C–O groups in GBA coordinate with uncoordinated Pb 2+ ions through strong interactions. Simultaneously, the hydrogen bonds between GBA and dimethyl sulfoxide slow down solvent volatilization during annealing, thereby delaying phase transitions. Additionally, the hydrophobic benzene rings in GBA create a protective surface layer that shields the perovskite from moisture ingress, thus preventing the formation of the detrimental photoinactive δ-phase. This multifunctional passivation agent effectively reduces the surface defect state density of CsPbI 1.8 Br 1.2 while simultaneously promoting grain enlargement and extending charge carrier lifetimes. Such strategic modifications significantly suppress nonradiative recombination processes, resulting in HTL-free C-IPSCs with enhanced photovoltaic performance. The optimized devices demonstrate a remarkable efficiency increase from 12.03% to 14.34%, coupled with improved long-term stability. This work highlights the synergistic role of GBA in regulating crystallization and passivating defects, thereby presenting a promising strategy for the development of high-performance HTL-free C-IPSCs.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.