Using an Innovative Bifunctional Siloxane to Protect Cement Composite Surfaces from Biological Corrosion

Le résumé fourni par la source

This study tested the effectiveness of a bifunctional polysiloxane (L43) as a means of protecting concrete surfaces from biocorrosion. L43 was designed to contain two types of functional groups in its structure: surface-active hydrophobic chains and hydrophilic groups that allow the coating to permanently bond to the concrete. L43-coated cement samples achieved compressive strengths exceeding 70 MPa, while samples subjected to cyclic freeze-thaw tests achieved compressive strengths exceeding 33 MPa. In addition, compound L43 at a concentration of 5% reduced the photosynthetic activity of microalgae cells on the concrete surface. The maximum value of chlFI decreased by 69.5%, while the average value decreased by 71.4%. Thus, it was proven that compound L43 effectively counteracts biological corrosion without deteriorating the structure of the impregnated substrate. It should be emphasized that the biocidal effect is due to the structure of the siloxane compound and appropriately selected functional groups. There is no need to add harmful biocides, making the solution environmentally friendly. In addition, the coating allows for free air circulation, which is crucial for the protection of building and construction materials.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.