Some initial results on modification of aC:H films by UV-C irradiation
Rattachement africain : bg. Niveau de preuve : code pays fourni par la source.
Le résumé fourni par la source
Abstract In the present work, we present the results of processing of aC:H thin films (deposited on Si (001) substrates covered with 330 nm thin film of SiO2) with UV-C irradiation from mercury UV-C lamp (λ = 254 nm, power of 38 W). The UV-C treatment time of the different samples was 2.5, 5, 10, 15, 30, 45, 60, 90, 120, 180 or 360 minutes respectively, and the samples were irradiated in an air atmosphere. The obtained films were characterized by Raman spectroscopy and X-ray photoelectron spectroscopy (XPS). A gradual decrease of oxygencontaining radicals and the fraction of sp3 hybridized carbon was found with increasing the UV-C irradiation time up to 90 min, after which a reverse process of increasing these phases in aC:H films was observed.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Le contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé ; titre concordant.
- Titre Crossref
- Some initial results on modification of aC:H films by UV-C irradiation
- Date Crossref
- 01/04/2025
- Éditeur
- IOP Publishing
- Type
- journal-article
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude, et il ne compte pas comme une seconde source scientifique indépendante.
Les institutions déclarées
Une affiliation ne permet pas de déduire la nationalité d’un auteur.