A Novel Sulfonated Polyimide Composite Membrane Containing Covalent Organic Frameworks for Iron–Chromium Redox Flow Battery Application

Le résumé fourni par la source

Iron–chromium redox flow batteries (ICRFB), as the pioneering technology in flow battery energy storage, have regained research attention with advancements in the field. Despite their significant cost advantage, the capacity degradation due to ion crossover through ion exchange membranes remains a major barrier to commercialization. In addition, there are relatively few types of nonfluorinated ion exchange membrane materials currently reported in ICRFB. Herein, covalent organic frameworks, sulfonated Schiff base network type (SSNW), were introduced into sulfonated polyimide (SPI) to prepare a novel SPI/SSNW composite membrane for ICRFB. The hydrogen bonding network formed by the −SO 3 H group in SPI and SSNW, with the fluorine atoms in SPI and the nitrogen atoms in SSNW, as well as the size exclusion effect of the SSNW, effectively hinder the permeation of Cr 3+ and Fe 3+, which was further analyzed by electrostatic potential calculation. Single-cell performance tests revealed that ICRFB equipped with SPI/SSNW-1% membrane achieved 93.96% Coulombic efficiency and 76.40% energy efficiency at 80 mA cm –2 . Compared with the Nafion212 membrane, the SPI/SSNW-1% membrane exhibited 17.74% higher capacity retention over 50 cycles. These results demonstrate that optimized sulfonated polyimide composite membranes are promising candidates for ICRFB applications.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.