Experimental Investigation of the Mechanical and Electrical Failure of the Electrode Tab of Lithium-Ion Pouch Cells Under Quasi-Static Mechanical Load

Le résumé fourni par la source

The electrode tabs of pouch cells are rigidly joined to the bus bar in a battery module to achieve an electric connection. The effect of abusive mechanical loads arising from crash-related deformation or the possible movement of battery cells caused by operation-dependent thickness variations has so far never been investigated. Three quasi-static abuse tests for the anode and cathode electrode tabs were conducted with pouch cells at 100% SOC. Tensile tests on the anode, cathode and pouch foil were performed in order to explain differences between the anode and cathode in the abuse tests. The experiments revealed different failure mechanisms for the anode and cathode electrode tabs. The cathode failed at an average maximum load of 940.3 N through an external rupture of the electrode tab. The anode failed at an average maximum load of 868.9 N through a rupture of the single electrode sheets and the opening of the pouch foil. No thermal runaway occurred for either cathode or anode. The results of this study reveal a more critical failure behavior for the anode electrode tab, which can be addressed in the future by adding a predetermined breaking point and adapting the geometry of the anode electrode tab.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.