Inter‐tow toughness modification of carbon fiber reinforced cyanate resin matrix composites

Le résumé fourni par la source

Abstract Carbon fiber‐reinforced cyanate ester resin matrix composites (CF/CE) are widely used in aerospace for their high‐temperature resistance and wave‐absorbing properties. However, CF/CE is prone to interlaminar delamination during the curing molding process or practical applications due to the brittleness of CE resin. In this study, we use polyether sulfone (PES) as a toughening layer through the inter‐tow toughening method to prepare PES inter‐tow toughened CF/CE (CF/CE‐P) and to investigate their thermal, mechanical, and microscopic morphology. We find that CF/CE‐P has a higher glass transition temperature ( T g ) and a lower coefficient of thermal expansion (CTE) than those of CF/CE composites. The flexural strength, flexural modulus, interlaminar shear strength (ILSS), and impact toughness of CF/CE‐P with 15 wt% PES is increased by 34%, 15%, 34%, and 45%, respectively, compared to CF/CE. In addition, the mode I interlaminar fracture toughness ( G IC ) of CF/CE‐P with 15 wt% PES is 1.86 times that of CF/CE. Highlights The inter‐tow toughening technique on a three‐dimensional scale is proposed. Model I interlaminar fracture toughness increased by 86% after inter‐tow toughness modification carbon fiber‐reinforced cyanate ester resin matrix composites. The composite material exhibits improved toughness and thermal performance. The prepreg preparation process is suitable for continuous industrial production.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.