Molten Salt Assisted Assembly (MASA) of novel mesoporous Ni0.5Mn0.5Co2O4 for high-performance asymmetric supercapacitors

Le résumé fourni par la source

• The first synthesis of mesoporous Ni 0.5 Mn 0.5 Co 2 O 4 , achieved through the MASA method. • Ni 0.5 Mn 0.5 Co 2 O 4 exhibits a relatively high surface area and improved redox activity. • Ni 0.5 Mn 0.5 Co 2 O 4 shows a significantly high capacitance compared to NiCo 2 O 4 and MnCo 2 O 4. Mesoporous transition metal oxides (TMO) are immensely investigated as electrode materials in supercapacitors. The molten salt assisted self-assembly (MASA) process enables a facile route for the synthesis of the mesoporous TMO. In this study, mesoporous nickel manganese cobaltite (Ni 0.5 Mn 0.5 Co 2 O 4 ) is synthesized for the first time using a MASA process and is evaluated as a novel electrode-active material for asymmetric supercapacitors. The objective of this work is to quantitatively measure the performance improvement in the Ni 0.5 Mn 0.5 Co 2 O 4 electrode based on its composition and reveal the improvement mechanism through electrochemical methods. The electrochemical performance of the NiCo 2 O 4 and MnCo 2 O 4 prepared by MASA is also investigated, in order to understand the synergistic effect of Ni and Mn elements in the same cobaltite structure. In line with the data obtained from half cells, a full asymmetric cell is prepared by assembling the appropriate amount of Ni 0.5 Mn 0.5 Co 2 O 4 and activated carbon through the charge balance theory. The test results show that the specific capacitance C A ( C s ) values are 2.62F/cm 2 (92.1F/g) for mesoporous NiCo 2 O 4 , 0.26F/cm 2 (9.8F/g) for mesoporous MnCo 2 O 4 , and 9.53F/cm 2 (338.5F/g) for mesoporous Ni 0.5 Mn 0.5 Co 2 O 4 under the test conditions of 5 mA/cm 2 . The asymmetric supercapacitor assembled with Ni 0.5 Mn 0.5 Co 2 O 4 and activated carbon demonstrates a superior energy density of 79.52 Wh/kg at 1 mA/cm 2 . The findings of the study highlight the importance of substituting the electrode with Ni 0.5 Mn 0.5 Co 2 O 4 to enhance the C A ( C s ) by achieving proper surface properties and electrochemical activity.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.