Over 300 mW Single-Frequency Distributed Bragg Reflector Fiber Laser at 2.04 μm Based on Tm:YAG/Ho:YAG Co-Derived Silica Fiber
Résumé fourni par la source
Several Tm:YAG/Ho:YAG co-derived silica fibers (THCDSFs) were fabricated using the molten core (MC) method. A maximum gain coefficient of 5.16 dB/cm at 2040 nm was obtained for the THCDSF prepared through the utilization of a spliced piece of semi-cylindrical 15.0 at% Tm:YAG and 2.5 at% Ho:YAG crystals as the core precursor material. Employing a 2.0-cm-long THCDSF and in-band pumping with a 1610 nm fiber laser, a stable single-frequency distributed Bragg reflector (DBR) laser operating at 2040 nm was demonstrated. The fiber laser has a maximum output power of 306 mW and a slope efficiency of 19.3% for the absorbed pump power. To the best of our knowledge, this represents the maximum recorded output power of a single-frequency dBR short-cavity laser oscillator above 2 μm to be reported.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé ; titre concordant.
- Titre Crossref
- Over 300 mW Single-Frequency Distributed Bragg Reflector Fiber Laser at 2.04 μm Based on Tm:YAG/Ho:YAG Co-Derived Silica Fiber
- Date Crossref
- 15/01/2025
- Éditeur
- Institute of Electrical and Electronics Engineers (IEEE)
- Type
- journal-article
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude et ne compte pas comme une seconde source scientifique indépendante.
Institutions déclarées
Une affiliation ne permet pas de déduire la nationalité d’un auteur.