Geothermal Nano-SiO2 Waste as a Supplementary Cementitious Material for Concrete Exposed at High Critical Temperatures

Le résumé fourni par la source

waste (GNSW) for sustainable Portland-cement-based concrete was investigated to improve the properties of concrete exposed at high critical temperatures. Portland cement was partially replaced by 20 and 30 wt.% of GNSW. The partial replacement effect on Portland-cement-based concrete subjected to 350, 550, and 750 °C was evaluated by measuring the weight changes, ultrasonic pulse velocity, thermogravimetric and differential thermal analysis, X-ray diffraction, surface inspection, and scanning electron microscopy under residual conditions. The ultrasonic pulse velocity results showed that the GNSW specimens maintained suitable stability after being heated to 350 °C. The SEM analysis revealed a denser microstructure for the 20 wt.% of partial replacement of Portland cement by GNSW specimen compared to the reference concrete when exposed to temperatures up to 400 °C, maintaining stability in its microstructure. The weight losses were higher for the specimens with partial replacements of GNSW than the reference concrete at 550 °C, which can be attributed to the pozzolanic activity presented by the GNSW, which increases the amounts of CSH gel, leading to a much denser cementitious matrix, causing a higher weight loss compared to the reference concrete. GNSW is a viable supplementary cementitious material, enhancing thermal properties up to 400 °C due to its high pozzolanic activity and filler effect while offering environmental benefits by reducing industrial waste.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.