Preparation and Characterization of 1D, 2D, and 3D Shapes of Anisotropic Gold Nanoparticles

Résumé fourni par la source

In recent times, the scientific community has become interested in gold nanoparticles, namely in the anisotropic class. Based on their shapes, they fall into three categories: one-, two-, and three-dimensional. The synthesis and properties of three different anisotropic gold nanoparticle preparations - gold nanobipyramids (one-dimension, 1D), gold nanoprisms (two-dimension, 2D), and gold stars (three-dimension, 3D) - are shown in this research. Here, our group describes a chemical reduction method mediated by seeds. X-ray powder diffraction, transmission electron microscopy, scanning electron microscopy, and ultraviolet-visible spectroscopy were used to analyze the anisotropic gold nanoparticles. The average dimensions of the nanobipyramids were 64.27 ± 7.31 nm for length and 25.87 ± 2.56 nm for diameter, according to the data; the average dimensions of the gold nanoprisms and goldstars were 43.54 ± 5.61 nm and 31.35 ± 7.01 nm, respectively. Furthermore, following centrifugation purification, the yields of triangle and bipyramidal particles rose from 40% to over 60% and from 60% to 90%, respectively. It was established what the ideal parameter concentration was to create anisotropic gold nanoparticles in three dimensions: one, two, and three.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.