Effect of Boron on Stress Corrosion Resistance of S31254 Super‐Austenitic Stainless Steel After Cold Deformation
Rattachement africain : cn. Niveau de preuve : code pays fourni par la source.
Le résumé fourni par la source
The effect of boron (B) on stress corrosion resistance of S31254 in the presence of residual stresses has been studied. The microstructure and corrosion resistance of S31254 containing B at different levels of cold deformation are analyzed in this study. In the results, it is shown that B favors the improvement of deformation uniformity of S31254. The grain boundary (GB) and slip bands have better corrosion resistance at 5% deformation, and the overall corrosion resistance is better than that of the undeformed state, with smaller passivation current density and narrower width of GB corrosion grooves, especially for the 40B samples. At 30% deformation, the overall corrosion resistance of 40B S31254 is better than 0B due to improved deformation uniformity.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Le contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé ; titre concordant.
- Titre Crossref
- Effect of Boron on Stress Corrosion Resistance of S31254 Super‐Austenitic Stainless Steel After Cold Deformation
- Date Crossref
- 16/07/2024
- Éditeur
- Wiley
- Type
- journal-article
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude, et il ne compte pas comme une seconde source scientifique indépendante.
Les institutions déclarées
Une affiliation ne permet pas de déduire la nationalité d’un auteur.