Axial Impact Resistance of High-Strength Engineering Geopolymer Composites: Effect of Polyethylene Fiber Content and Strain Rate

Le résumé fourni par la source

High-strength engineered geopolymer composite (EGC) materials exhibit excellent mechanical properties under quasistatic loading, thus showing great potential in military and civilian facilities subjected to impact or explosive loading. However, its dynamic mechanical response under high-speed loading is not fully understood. In this study, dynamic compressive test was performed on EGC with PE fiber contents of 0%, 0.5%, 1.0%, 1.5%, and 2.0% using the Split Hopkinson Pressure Bar (SHPB) test. The results indicated that EGC reinforced with 1.5% fiber exhibited optimal static and dynamic mechanical performance. In the strain rate range of 181 s−1 to 201 s−1, when the fiber content increased from 1.0% to 1.5% and 2.0%, the dynamic compressive strength of the EGC increased by 24.3%, 28.8%, and 44.0%, respectively, compared to the matrix without fiber. Dynamic parameters of the EGC, including dynamic compressive strength, dynamic increase factor, and impact toughness, showed sensitivity to strain rates and increased with strain rate. A modified model, incorporating the fiber bridging effect, was proposed based on the CEB-FIP model, providing important guidance for practical engineering applications.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.