Dynamic pressure scuffing initiation of a grade 250 flake graphite cast iron

Le résumé fourni par la source

The dynamic contact pressures experienced at the ring-liner interface of an engine are difficult to replicate in laboratory based reciprocating tribometers utilising a sliding Hertzian line contact, not least due to wear of the mating surfaces. A grade 250 flake graphite cast iron flat plate test geometry was designed to allow dynamic contact pressures between 8 and 62 MPa experienced in a heavy-duty diesel engine liner to be achieved on a reciprocating tribometer during the compression and expansion stroke.A constant normal load of 311 N was applied by sliding at 25 mm stroke length in PAO4 at 15 Hz against a 52100 rectangular contact area (2 × 20 mm). The temperature was slowly increased at 4 °C/min to initiate scuffing between the mating surfaces. Severe scuffing initiated at 250.8 ± 2.6 °C for all specimens. The spatially resolved friction force and non-contact optical profilometry suggested scuffing did not always initiate in the region of the highest contact pressure, whilst electron microscopy revealed that subsequent to lubricant failure, a transient low friction iron oxide layer was formed prior to removal and catastrophic adhesive wear.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.