Joining of Zirconium Alloys to Nickel Bearing Alloys for In-Core Components

Le résumé fourni par la source

Abstract Zirconium alloys are well-positioned as the material of choice for nuclear in-core structures since they have a low neutron absorption cross section and possess good material properties under elevated neutron flux and high-temperature operating conditions. The Canadian supercritical water-cooled reactor (SCWR) concept pressure tube includes a transition from zirconium-tin alloy (Excel) to a yet to be selected stainless steel to allow it to be seal welded to the inlet plenum. Thus, a method to join zirconium and its alloys to ferrous and nickel-bearing alloys is desired. To this end, a series of experiments were carried out to demonstrate the feasibility of this method. A joint approaching the strength of the parent material was achieved using both rotary friction welding and co-extrusion methods, although the joints exhibited lower ductility than that of the parent material. Microstructural examination of the joint revealed a ∼200 nm to ∼1 μm intermetallic layer at the transition zone, which was the location of failure in the tensile specimen.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.