Improved crystallisation of polysilazane‐derived Si 3 N 4 /SiC nanocomposites with Fe 2 O 3 catalyst
Rattachement africain : cn. Niveau de preuve : code pays fourni par la source.
Le résumé fourni par la source
Abstract In the present study, the use of a 3 wt% Fe 2 O 3 catalyst improved the crystallisation of polysilazane PSN2. Crystallisation peaks of higher intensity were observed for Si 3 N 4 and SiC at 1250 °C by using a 3 wt% Fe 2 O 3 catalyst than at 1500 °C without Fe 2 O 3 . Besides, the effects of temperature on the morphology of the samples were determined through scanning electron microscopy. Porous structures were observed at 1250 °C and these structures were transformed to flaky and near‐spherical nanoparticles as the temperatures were increased to 1350 and 1450 °C, respectively. Finally, the mechanism of Fe origination from Fe 2 O 3 reduction, the production of a supersaturated liquid alloy, and the release and diffusion of N 2 were proposed for Si 3 N 4 formation.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Le contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé, mais le titre doit être comparé manuellement.
- Titre Crossref
- Improved crystallisation of polysilazane‐derived Si <sub>3</sub> N <sub>4</sub> /SiC nanocomposites with Fe <sub>2</sub> O <sub>3</sub> catalyst
- Date Crossref
- 20/04/2021
- Éditeur
- Institution of Engineering and Technology (IET)
- Type
- journal-article
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude, et il ne compte pas comme une seconde source scientifique indépendante.
Les institutions déclarées
Une affiliation ne permet pas de déduire la nationalité d’un auteur.