Synthesis and Electrochemical Performance of Ni Substituted SrTi0.3Fe0.7O3-δ Cathode: Effect of A-Site Deficiency
Rattachement africain : cn. Niveau de preuve : code pays fourni par la source.
Le résumé fourni par la source
Herein, we present the synthesis and electrochemical properties of Ni substituted Sr 1-x Ti 0.3 Fe 0.6 Ni 0.1 O 3-δ (STFN, x=0; STFN-5, x=0.05) as solid oxide fuel cell cathodes. First, the results suggest a Ni solubility limit in SrTi 0.3 Fe 0.7 O 3-δ , lower than ~14 at% in B-site. Second, the conductivities increase first with temperature increasing and then decrease; STFN shows a maximum conductivity of 23.9 S/cm at 700 o C, while STFN-5 shows similar peak value but at much lower temperature of ~600-650 o C. Third, the electrochemical impedance spectroscopy tests are conducted in a wide range of oxygen partial pressures below 0.21 atm, using symmetrical cells. The A-site deficient STFN-5 cathode shows smaller polarization resistance values compared with A-site stoichiometric composition. The polarization resistance of STFN-5 is ~0.11 Ω·cm 2 at 750 o C in oxygen partial pressure of 0.21 atm and shows a relative stable operation during long term test in air.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Le contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé, mais le titre doit être comparé manuellement.
- Titre Crossref
- Synthesis and Electrochemical Performance of Ni Substituted SrTi<sub>0.3</sub>Fe<sub>0.7</sub>O<sub>3-δ</sub> Cathode: Effect of A-Site Deficiency
- Date Crossref
- 10/07/2019
- Éditeur
- The Electrochemical Society
- Type
- journal-article
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude, et il ne compte pas comme une seconde source scientifique indépendante.
Les institutions déclarées
Une affiliation ne permet pas de déduire la nationalité d’un auteur.