Rattachement africain : br. Niveau de preuve : code pays fourni par la source.
Le résumé fourni par la source
In this work, (K0.48Na0.52)NbO3 (KNN) ceramics were prepared by using Spark Plasma Sintering (SPS) method applying different heating rates. The microstructural evolution of the ceramics was analyzed and the results were correlated with possible sintering mechanisms. The analysis revealed homogeneous microstructures with nanometric grains. It was noticed that with increasing the heating rate the grain size decreases and the bimodal grain growth is suppressed. The Master Sintering Curve was constructed and an apparent activation energy of 660 kJ/mol was determined. From this result, it was possible to predict the possible densification mechanisms present in the KNN by SPS route.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Le contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé, mais le titre doit être comparé manuellement.
- Titre Crossref
- Sintering kinects of (K<sub>0.48</sub>Na<sub>0.52</sub>)NbO<sub>3</sub>lead-free piezoelectric ceramics densified by spark plasma sintering: Construction of master sintering curve
- Date Crossref
- 11/06/2019
- Éditeur
- Informa UK Limited
- Type
- journal-article
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude, et il ne compte pas comme une seconde source scientifique indépendante.
Les institutions déclarées
Une affiliation ne permet pas de déduire la nationalité d’un auteur.