Retained austenite stabilisation in low carbon high silicon steel during isothermal holding
Rattachement africain : cn, us. Niveau de preuve : code pays fourni par la source.
Le résumé fourni par la source
We elucidate here the role of isothermal hold temperature of 300–500°C after intercritical annealing at 760°C on bainitic transformation and in governing the stabilisation of retained austenite in a 0.23C-1.35Si-1.82Mn steel. A critical analysis was attempted to explain the observations using displacive mechanism of bainite formation in the attempt to endeavour to understand the kinetics of bainitic transformation during isothermal holding. The model predicted that carbon enrichment in austenite was of particular significance in governing the stability of retained austenite. Thus, through the contribution of transformation induced plasticity effect of retained austenite, high tensile strength (964 MPa) and excellent ductility (uniform elongation of 24.5% and total elongation of 32%) was obtained on isothermal holding at 400°C.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Le contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé ; titre concordant.
- Titre Crossref
- Retained austenite stabilisation in low carbon high silicon steel during isothermal holding
- Date Crossref
- 01/01/2019
- Éditeur
- SAGE Publications
- Type
- journal-article
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude, et il ne compte pas comme une seconde source scientifique indépendante.
Où se fait cette recherche
-
University of Science and Technology Beijing Collaborative Innovation Center of Steel Technology pays non établi dans la noticeUniversité ou école supérieure
-
The University of Texas at El Paso Laboratory for Excellence in Advanced Steel Research pays non établi dans la noticeUniversité ou école supérieure
-
State Key Laboratory of Metal Material for Marine Equipment and Application pays non établi dans la noticeStructure de recherche
-
State Key Laboratory of Metal Materials for Marine Equipment and Applications pays non établi dans la noticeStructure de recherche
Collaborative Innovation Center of Steel Technology — University of Science and Technology Beijing, Laboratory for Excellence in Advanced Steel Research — The University of Texas at El Paso et State Key Laboratory of Metal Material for Marine Equipment and Application, avec 1 autre affiliation.
Une affiliation ne permet pas de déduire la nationalité d’un auteur.