Photoluminescent properties of Eu-doped ZnLiNbO 4
Rattachement africain : tw. Niveau de preuve : code pays fourni par la source.
Le résumé fourni par la source
In this study, fluorescent Eu 3+ -doped ZnLiNbO 4 materials were prepared via a vibrating milled solid-state reaction method. The objective was to develop new fluorescent oxide materials and study their fluorescent properties. The ZnLiNbO 4 tetragonal spinel structure was formed with a single phase at a sintering temperature of 800 °C and with a regular shape at 1000 °C. The main exciton band was at 466 nm ( 7 F 0 → 5 D 2 ), and the main emission band was at 615 nm ( 5 D 0 → 7 F 2 ), which was an orange–red light band. The emission intensity was approximately 5% when the doping concentration reached 7%. The decay time was 2.96 ms.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Le contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé, mais le titre doit être comparé manuellement.
- Titre Crossref
- Photoluminescent properties of Eu-doped ZnLiNbO <sub>4</sub>
- Date Crossref
- 18/04/2018
- Éditeur
- IOP Publishing
- Type
- journal-article
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude, et il ne compte pas comme une seconde source scientifique indépendante.
Les institutions déclarées
Une affiliation ne permet pas de déduire la nationalité d’un auteur.