Effect of Reversed Austenite on the Stress Corrosion Cracking of Modified 17-4PH Stainless Steel
Rattachement africain : cn, jp. Niveau de preuve : code pays fourni par la source.
Le résumé fourni par la source
A study has been conducted investigating the effect of reversed austenite on the stress corrosion cracking property of a chemically modified 17-4PH with specially designed two-step tempering in a simulated geothermal environment. Two specimens with very similar 0.2% proof stress and different contents of reversed austenite were used to study the effect of reversed austenite on stress corrosion cracking (SCC). Slow strain rate testing (SSRT) with hydrogen precharged specimens and under cathodic polarization confirmed the detrimental effect of reversed austenite on hydrogen embrittlement. SSRT under anodic polarization confirmed the involvement of active path corrosion in the SCC of modified 17-4PH in a simulated geothermal environment, and showed that the effect of reversed austenite on active path corrosion was also detrimental. However, SSRT was not able to resolve the most impacted SCC property, SCC initiation, or SCC propagation.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Le contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé ; titre concordant.
- Titre Crossref
- Effect of Reversed Austenite on the Stress Corrosion Cracking of Modified 17-4PH Stainless Steel
- Date Crossref
- 17/01/2017
- Éditeur
- Association for Materials Protection and Performance (AMPP)
- Type
- journal-article
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude, et il ne compte pas comme une seconde source scientifique indépendante.
Les institutions déclarées
Une affiliation ne permet pas de déduire la nationalité d’un auteur.