Fatigue Crack Propagation in Polycarbonate
Rattachement africain : us, in. Niveau de preuve : code pays fourni par la source.
Le résumé fourni par la source
We investigated the effects of various material and fatigue parameters on crack-growth rate per cycle, da/dn, as a function of stress intensity factor range, ΔK. In contrast to other common polymers the frequency (0.1-20 Hz) or wave form has little effect on fatigue crack propagation (FCP) of polycarbonate. However, mean stress is significant, with FCP curves shifted towards higher ΔK values for higher mean stresses. Environment is also significant; water induces a discontinuity in the FCP curves. Thermal history is important; annealing at temperatures below T g causes complex changes in FCP behavior. Some changes such as minima in plots of ΔK at fracture and fracture energy as a function of annealing temperature can be correlated with calorimetric (DSC) data which suggest competitive ordering-disordering effects caused by annealing.
Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.
Le contrôle bibliographique ouvert
DOI retrouvé dans Crossref DOI retrouvé ; titre concordant.
- Titre Crossref
- Fatigue Crack Propagation in Polycarbonate
- Date Crossref
- 01/06/1976
- Éditeur
- AMERICAN CHEMICAL SOCIETY
- Type
- book-chapter
Ce recoupement confirme des métadonnées liées au DOI. Il ne confirme ni la méthode ni les conclusions de l’étude, et il ne compte pas comme une seconde source scientifique indépendante.
Les institutions déclarées
Une affiliation ne permet pas de déduire la nationalité d’un auteur.