Combustion synthesis and stability of nanocrystalline La_2O_3 via ethanolamine-nitrate process

Résumé fourni par la source

Pure nanocrystalline La2O3 powders were successfully prepared by the combustion method.The effect of ethanolamine-to-nitrate ratio on phase composition and crystallite size of the combustion products was systematically investigated.Pure hexagonal La2O3 powders were almost formed in stoichiometric reaction（ψ=1.15）,while metallic La phase was obtained in fuel-rich conditions（ψ≥3.0）.The as-synthesized hexagonal La2O3 was found to be chemically unstable in ambient air since a complete transformation to hexagonal La（OH）3 was detected after 24 h exposure to air.The resulting hexagonal La（OH）3 showed an excellent ability to remove water pollutant and could nearly remove 100% of the Congo red at room temperature with a removal capacity of 143.5 mg Congo red/g.The phosphate adsorption data on hexagonal La（OH）3 agreed well with the Langmuir model with the estimated maximum adsorption capacity of 57.8 mg/g.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.