Fabrication and testing of Rutherford-type cables for react and wind accelerator magnets

Le résumé fourni par la source

A common coil design for a high-field accelerator dipole magnet using a Nb/sub 3/Sn cable with the React-and-Wind approach is pursued by a collaboration between Fermilab and LBNL. The design requirements for the cable include a high operating current so that a field of 10-11 T can be produced, together with a low critical current degradation due to bending around a 90 mm radius. A program, using ITER strands of the internal tin type, was launched to develop the optimal cable design for react-and-wind common coil magnets. Three prototype cable designs, all 15 mm wide, were fabricated: a 41-strand cable with 0.7 mm diameter strands; a 57-strand cable with 0.5 mm diameter strands; and a 259-strand multi-level cable with a 6-around-1 sub-element using 0.3 mm diameter wire. Two versions of these cables were fabricated: one with no core and one with a stainless steel core. Additionally, the possibility of a wide (22 mm) cable made from 0.7 mm strand was explored. This paper describes the first results of the cable program including reports on cable fabrication and reaction, first winding tests and first results of the measurement of the critical current degradation due to cabling and bending.

Ce résumé expose les affirmations des auteurs. BNTIC ne l’interprète pas comme une validation indépendante des résultats.